Welding Terminologies 2g3a11

Welding Terminologies actual throat - The shortest distance between the weld root and the face of the fillet weld. back weld - A weld made at the back of a single groove welded t after the completion of the groove weld. backing - A material or deviced placed against the back side of the t, or at both side of the weld in electroslag and electrogas welding, to and retain molten weld metal. the material maybe partially fused or remain unfused during welding and maybe either metal or nonmetal. backing weld - Backing in the form of a weld made from primary weld. bevel - An angular edge shape. complete t penetration - A t root condition in a groove weld in which weld metal extends completely trhough the t thickness. corner t - A t betwen two located approximately at right angles to each other in the form of an L. depth of bevel - The perpendicular distance from the base metal surface to the root edge or the begining of th root face. depth of fusion - The distance that fusion extends into the base metal or previous bead from the surface melted during welding. edge t - A t betwen the edges of two or more parallel or nearly parallel . edge preparation - The preparation of the the edges of the t , cutting, cleaning, plating, or other means. edge weld - A weld in an edge t, a flange butt t or a flange corner t in which the full thickness of the are fused. effective throat - The minimum distance minus any convexity, betwen the weld root and the face of a fillet weld. face reinforcement - Weld reinforcement on the side of the t from which welding was done. fillet weld - A weld of approximately traingular cross section ing two surfaces approximately at right angles to each other in a lap-, T-, or corner t. fillet weld leg - The distance from the t root to the toe of the fillet weld. fusion - The melting together of filler metal and base metal, or base metal only, to produce a weld. fusion face - A surface of th base metal that will be melted during welding or the area of base metal melted as determined on the cross section of the weld.

groove angle - The total included angle of the groove between workpieces. In ts where both edges of the workpieces are prepared at an angle this dimension is the total of both. groove weld - A weld in a groove between workpieces. t - The junction of or the edges of that are to be ed or had been ed. t design - The shape, dimensions and configuration of the t. t filler - A metal plate inserted between a splice member and a thinner t member to accommodate t of dissimilar thickness in a spliced butt t. t geometry - The shape and dimensions of a t in cross section prior to welding. t type - A weld t classification base on five basic t configurations such as butt t, corner t, edge t, lap t and T-t.

Electrical Characteristics To supply the electrical energy necessary for arc welding processes, a number of different power supplies can be used. The most common classification is constant current power supplies and constant voltage power supplies. In arc welding, the voltage is directly related to the length of the arc, and the current is related to the amount of heat input. Constant current power supplies are most often used for manual welding processes such as gas tungsten arc welding and shielded metal arc welding, because they maintain a relatively constant current even as the voltage varies. This is important because in manual welding, it can be difficult to hold the electrode perfectly steady, and as a result, the arc length and thus voltage tend to fluctuate. Constant voltage power supplies hold the voltage constant and vary the current, and as a result, are most often used for automated welding processes such as gas metal arc welding, flux cored arc welding, and submerged arc welding. In these processes, arc length is kept constant, since any fluctuation in the distance between the wire and the base material is quickly rectified by a large change in current. For example, if the wire and the base material get too close, the current will rapidly increase, which in turn causes the heat to increase and the tip of the wire to melt, returning it to its original separation distance. The direction of current used in arc welding also plays an important role in welding. Consumable electrode processes such as shielded metal arc welding and gas metal arc welding generally use direct current, but the electrode can be charged either positively or negatively. In welding, the positively charged anode will have a greater heat concentration and, as a result, changing the polarity of the electrode has an impact on weld properties. If the electrode is positively charged, it will melt more quickly, increasing weld penetration and

welding speed. Alternatively, a negatively charged electrode results in more shallow welds. Non-consumable electrode processes, such as gas tungsten arc welding, can use either type of direct current, as well as alternating current. With direct current however, because the electrode only creates the arc and does not provide filler material, a positively charged electrode causes shallow welds, while a negatively charged electrode makes deeper welds. Alternating current (AC) rapidly moves between these two, resulting in mediumpenetration welds. One disadvantage of AC, the fact that the arc must be re-ignited after every zero crossing, has been addressed with the invention of special power units that produce a square wave pattern instead of the normal sine wave, eliminating low-voltage time after the zero crossings and minimizing the effects of the problem. POLARITY SMAW DCEP

GTAW DCEN

GMAW DCEP

FCAW

SAW

DCEP

DCEP

DCEP - Direct Current Electrode Positive or Reverse Polarity DCEN - Direct Current Electrode Negative or Straight Polarity

Postweld Heat Treatment Temperature Range Base Metal P-No. and Group P-No.

Base Metal Group

Metal Temperature Range (°C) ASME B31.3 Table 331.1.1

ASME B31.1 Table 132

ASME VIII Table UCS-56

1

Carbon steel

593-649

600-650

650 min.

3

Alloy steels, Cr ≤ ½ %

593-718

600-650

595 min.

4

Alloy steels, ½% < Cr ≤ 2%

704-746

700-750

650 min.

Alloy steels (2¼% ≤ Cr ≤ 10%)

704-760

700-760

675 min. for 5A,5B,5C Gr 1, 705 min. for 5B Gr 2

6

High alloy steel martensitic A240 Gr 429

732-788 621-663

760-800 Not mentioned

Not mentioned

7

High alloy steel ferritic

None

730-775

Not mentioned

8

High alloy steel austenitic

None

None

Not mentioned

593-635

600-650 for 9A 600-630 for 9B

595 min.

5A,5B,5C

9A,9B

Nickel alloy steels

10(A/B/C/K/J) Cr-Cu steels

760-816

Not mentioned

595 min for 10A 650 min. for 10B 540 min. for 10C 540 min. for 10H

See Table 331.1.1 Note (7)

See Table 132 General Note (I)

Not mentioned

10H

Duplex stainless steels

10I

27Cr steels

663-704

730-815

Not mentioned

11A SG1

8Ni, 9Ni steels

552-585

Not mentioned

Not mentioned

11B SG2

5Ni steel

552-585

Not mentioned

Not mentioned

Zr R60705

538-593

Not mentioned

Not mentioned

62 Time Range

Gas The properties of gases affect the performance of all welding processes. The ionization potential of the shielding gas influences the ease of arc initiation and stability. Thermal conductivity of a gas determines the voltage and energy constant of the arc. Gases such as carbon dioxide can have higher heat conductivity than helium at arc temperatures because of the effect of disassociation and recombination. Reactive and oxidizing gases such as carbon dioxide (CO2) and oxygen (O2) can have detrimental effects on base metals such as aluminum, nickel, titanium, zirconium, and tungsten. For this reason, carbon dioxide or oxygen cannot be used as the shielding gas for gas tungsten arc welding. Proper gas selection is crucial to efficient welding in the most cost-effective manner. Many factors must be considered. These are not limited to the following: a. b. c. d. e. f. g. h. i. j. k. l. m. n.

Type and thickness of base metal being welded Arc characteristics Metal transfer Travel speed Depth and width of fusion Cost of welding Mechanical properties Cleanliness of the basemetal Spatter Arc cleaning action Gas purity t configuration Welding position Fume generation

Gas Mixture

Flow Rate Backing Gas Shielding Gas Trailing Gas Search

Preheat Preheat Temp. Min - Minimun preheat temperature as required per base metal thickness and/or basemetal P-No. prehet requirement. Inter Temp. Max - Maximum inter temperature. Preheat Maintenance - As required, preheat temperature must be maintained and preheat maintenance method shall be specified in the WPS.

All rights reserved Copyright © 2008

Filler Metals Spec.No.(SFA) - It's the ASME designated Specification.

SFA-5.1 SFA-5.2 SFA-5.3 SFA-5.4 SFA-5.5 SFA-5.6 SFA-5.7 SFA-5.8 SFA-5.9 SFA-5.10 SFA-5.11 SFA-5.12 SFA-5.13 SFA-5.14 SFA-5.15 SFA-5.16

List of ASME Designated Filler Metal Specification Carbon Steel Electrodes for Shielded Metal Arc Welding Carbon and Low Alloy Steel Rods for Oxyfuel Gas Welding Aluminum and Aluminum-Alloy Electrodes for Shielded Metal Arc Welding Stainless Steel Electrodes for Shielded Metal Arc Welding Low-Alloy steel Electrodes for Shielded Metal Arc Welding Covered Copper and Copper Alloy Arc Welding Electrodes Copper and Copper Alloy Bare Welding Rods and Electrodes Filler Metal for Brazing and Braze Welding Bare Stainless Steel Welding Electrodes and Rods Bare Aluminum and Aluminum-Alloy Welding Electrodes and Rods Nickel and Nickle-Alloy Welding Electrodes for Shielded Metal Arc Welding Tungsten and Tungsten-Alloy Electrodes for Arc Welding and Cutting Surfacing Electrodes for Shielded Metal Arc Welding Nickle and Nickle-Alloy Bare Welding Electrodes and Rods Welding Electrodes and Rods for Cast Iron Titanium and Titanium-Alloy for Welding Electrodes and Rods

SFA-5.17 SFA-5.18 SFA-5.20 SFA-5.21 SFA-5.22 SFA-5.23 SFA-5.24 SFA-5.25 SFA-5.26 SFA-5.28 SFA-5.29 SFA-5.30 SFA-5.31 SFA-5.32

Carbon Steel Electrodes and Fluxes for Submerged Arc Welding Carbon Steel Electrodes and Rods for Gas Shielded Arc Welding Carbon Steel Electrodes for Flux cored Arc Welding Bare Electrode and Rods for Surfacing Stainless Steel Electrodes for Flux Cored Arc Welding and Stainless Steel Flux Cored Rods for Gas Tungsten Arc Welding Low-Alloy Steel Electrodes and Fluxes for Submerged Arc Welding Zirconium and Zirconium-Alloy Welding Electrodes and Rods Carbon and Low-Alloy Steel Electrodes and Fluxes for Electroslag Welding Carbon and Low-alloy Steel Electrodes for Electrogas Welding Low-Alloy Steel Electrodes and Rods for Gas Shielded Arc Welding Low-Alloy Steel Electrodes for Flux Cored Arc welding Consumables Inserts Fluxes for Brazing and Braze Welding Welding Shielding Gases

AWS No.(Class) - AWS designated filler metal classification F-No. - Grouping of electrodes and welding rods for qualification. A-No. - Classification of ferrous weld metals analysis for procedure qualification.

Size of Filler metals(Ø) - Size of electrode(s) to be used is in diameter. One or more applicable eletrode sizes can be specified in the WPS Electrode-Flux (Class) - Applicable for Submerged Arc Welding (SAW) process Flux Trade Name - Applicable for Submerged Arc Welding (SAW) process Consumable Insert - Refer to SFA-5.30 of ASME II Part C for consumable insert specification Other - Weld metal thickness may be specified here or maximum allowable weld deposit per . All rights reserved

Base Metals P-No. and Group No. - Refer to the table for material groupings in ASME IX QW-422 Grouping of Base Metal for Qualification pages 69-130.

Base Metal P-No. and Groupings P-No.

Base Metal Group

1

Carbon steel

3

Alloy steels, Cr ≤ ½%

4

Alloy steels, ½% < Cr ≤ 2%

5A,5B,5C

Alloy steels (2¼% ≤ Cr ≤ 10%)

6

High alloy steel martensitic

7

High alloy steel ferritic

8

High alloy steel austenitic

9A,9B

Nickel alloy steels

10(A/B/C/K/J) Cr-Cu steels 10H

Duplex stainless steels

10I

27Cr steels

11A SG1

8Ni, 9Ni steels

11B SG2

5Ni steel

62

Zr R60705

Specification Type or Grade - base on the design or fabrication reference drawings write the base metal's Material Specification to be welded together and its Type or Grade that will be covered by the WPS. There are also steel material specifications that don't specify any type or grade like, SA-36 plate and shapes materials, SA-105 flanges & fittings materials and others. Chem. Analysis and Mech. Prop.(Optional) - chemical analysis and mechanical properties of the base metals to be welded. Thickness Range: GROOVE - The maximum base metal or weld metal thickness that can be welded and deposited respectively should depend on the base metal thickness(T) of the Procedure Qualification Test (PQR) test piece, plate or pipe; or deposited weld metal thickness(t) in the PQR test piece. Example, If test piece thickness(T) is 12 mm, the maximum thicknes(T) limit should be 24 mm.

For the minimum thickness limit, refer to QW-451.1 of ASME IX - Procedure Qualification Thickness Limits and Test Specimen FILLET - Once the PQR was done in groove weld unlimited thickness is qualified for fillet weld.

ts t Design - write what is the type of the t that will be prepared in production welding. Is it groove/butt t or fillet t? Your reference for appropriate t design should be the applicable fabrication detailed drawings. It is not necessary to write a very specific t design on this space, such as "Vee groove", "single bevel", "Tee t", etc. Either groove or fillet or groove and fillet would be understandable. You may just draw a detailed illustrations of the specific or typical t designs in the WPS and follow the note

on the sample below.

Backing - Mark the "(Yes)" space with "X" if there is a backing material to be provided prior to welding the initial or root . Mark the "(No)" space if there's none. For the t with combination of weld processes - the initial weld process can be consider as the backing of second welding process to be initiated. For example, in combined GTAW + SMAW processes the GTAW process is a backing of the SMAW process. Backing Material(Type) - Refer to both backing and retainers.

Welding Processes The AWS definition for a welding process is "a materials ing process which produces coalescence of materials by heating them to suitable temperatures with or without the application of pressure or by the application of pressure alone and with or without the use of filler material". AWS has grouped the processes together according to the "mode of energy transfer" as the primary consideration. A secondary factor is the "influence of capillary attraction in effecting distribution of filler metal" in the t. Capillary attraction distinguishes the welding processes grouped under "Brazing" and "Soldering" from "Arc Welding", "Gas Welding", "Resistance Welding", "Solid State Welding", and "Other Processes." Shielded Metal Arc Welding (SMAW) - also known as manual metal arc (MMA) welding or informally as stick welding, is a manual arc welding process that uses a consumable electrode coated in flux to lay the weld. An electric current, in the form of either alternating current or direct current from a welding power supply, is used to form an electric arc between the electrode and the metals to be ed. As the weld is laid, the flux coating of the electrode disintegrates, giving off vapors that serve as a shielding gas and providing a layer of slag, both of which protect

the weld area from atmospheric contamination. Gas Tungsten Arc Welding (GTAW) - also known as tungsten inert gas (TIG) welding] and was defined as "an arc welding process which produces coalescence of metals by heating them with an arc between a tungsten (non-consumable) electrode and the work piece. Shielding is obtained from a gas or gas mixture." It is an arc welding process that uses a nonconsumable tungsten electrode to produce the weld. The weld area is protected from atmospheric contamination by a shielding gas (usually an inert gas such as argon), and a filler metal is normally used, though some welds, known as autogenous welds, do not require it. A constant-current welding power supply produces energy which is conducted across the arc through a column of highly ionized gas and metal vapors known as a plasma. Gas Metal Arc Welding (GMAW) It was developed in the late 1940s for welding aluminum and has become extremely popular. It is defined as "an arc welding process which produces coalescence of metals by heating them with an arc between a continuous filler metal (consumable) electrode and the work piece. Shielding is obtained entirely from an externally supplied gas or gas mixture." The electrode wire for GMAW is continuously fed into the arc and deposited as weld metal. This process has many variations depending on the type of shielding gas, the type of metal transfer, and the type of metal welded.

Flux Cored Arc Welding (FCAW) It is defined as "an arc welding process which produces coalescence of metals by heating them with an arc between a continuous filler metal (consumable) electrode and the work piece. Shielding is provided by a flux contained within the tubular electrode." Additional shielding may or may not be obtained from an externally supplied gas or gas mixture. Submerged Arc Welding (SAW) process that made automatic welding popular. Submerged arc welding is defined as "an arc welding process which produces coalescence of metals by heating them with an arc or arcs between a bare metal electrode or electrodes and the work piece. Pressure is not used and filler metal is obtained from the electrode and sometimes from a supplementary welding rod." It is normally limited to the flat or horizontal position.