Ceramic and Glaze Colorants Pottery Glaze Colors and Factors That Affect Them By Beth Peterson Updated 06/02/18

Alyson Aliano/Photodisc/Getty Images Colors in glazes are affected by the clay, slips, stains, or underglazes below them. Most ceramic colors, however, are a result of metallic oxides being dispersed in the fabric of the glaze itself. Under varying circumstances, these colorants can give very different results.

The Three Main Factors Affecting Pottery Glaze Color There are a number of variables that can effect a glaze's color. These mainly fall within a group of three major factors. o

o

o

The composition of the glaze. This not only includes the colorants in the glaze, but also other glaze materials that interact and effect that colorant or combination of colorants. The temperature to which the glaze is fired. Some colorants are volatile and will dissipate into the kiln atmosphere if fired too high. Others give different colors at different temperatures. The kiln's atmosphere during firing and, in some cases, during cooling.

Chromium Oxide Chrome oxide can yield a variety of colors: red, yellow, pink, brown, and especially green. Chrome is volatile at cone 6 and above and may jump from pot to pot causing streaks and smoky effects. o o o o

Chrome-red: needs lead glaze fired at cone 08 or below. Extremely toxic; not for functional ware. Chrome-yellow: needs lead-soda glaze fired at cone 08 or below, or will begin turning green. Extremely toxic; not for functional ware. Chrome and zinc yield brown. Chrome plus tin yields pink, grayed pink, and warm browns. Color depends on proportions of these oxides in glaze and in relation to each other.

1

o

Small amounts of chrome plus cobalt can yield teals at cone 9 and higher when fired in reduction. Magnesia glazes aid in producing nice colors.

Cobalt Oxide and Cobalt Carbonate Cobalt is an extremely powerful colorant that almost always produces an intense blue. Cobalt carbonate tends to be used more by potters because it has a finer particle size and is less intense. o o

o o

In glazes with a high magnesia content, very small amounts of cobalt can give a range from pink through blue violet. Magnesia and cobalt in glazes fired at cone 9 or higher can yield blue mottled with red, pink, and purple. Very hard to control and duplicate due to the narrow temperature and atmospheric range. Cobalt and rutile can produce in mottled and streaked effects. Cobalt with manganese and iron will yield an intense black.

Copper Oxide and Copper Carbonate Copper is a strong flux which can make a glaze more glossy. At cone 8 and above, copper is volatile and can jump from pot to pot. Copper generally gives green in oxidation and red in reduction. Copper oxide is more intense than copper carbonate, as it contains more copper by weight. o o o o

In alkaline glazes, copper will produce turquoise. Copper yields a lovely range of greens in lead glazes. Copper increases lead's solubility. Toxic; not for functional ware. Copper in barium high-fired glazes produce intense blue and blue-green in both oxidation and reduction. Toxic; not for functional ware. Copper in low-fire raku glazes can yield metallic copper. Over time, however, the glaze will oxidize to green.

Iron Oxides in Clay Not many potters would challenge iron's place as the most important of the ceramic colorants. Iron's natural presence in most clay bodies produces clay colors ranging from light gray to deepest brown. Under clear glazes, ironcontaining clay bodies can show a very similar range of colors. Iron-containing clay bodies that have been fired but are not mature, such as bisqueware, often are a salmon or yellowish pink color. If a pot is glazed with

2

a lower-temperature glaze and fired below the clay body's maturity temperature, a salmon, ocher or reddish brown color will show through.

Iron Oxide Types Most iron used in glazes is introduced as red iron oxide (ferric oxide, Fe2O3). Yellow iron oxide is another form of ferric oxide; although its raw color is different, it is chemically identical to and acts the same as red iron oxide. Black iron oxide (ferrous oxide, Fe3O4) is courser and generally not used. Crocus martis is an impure iron oxide which can be used to produce speckled, rough, or spotty effects.

Iron Oxide in Glazes Generally speaking, iron produces warm colors ranging from light tan and straw to deep, rich browns. o o o o o

High-fire glazes containing bone ash and iron can yield persimmon reds and oranges. Iron and tin in high-fire glazes result in a mottled cream color, breaking to red-brown in thin areas. Iron fluxes in reduction atmospheres. It is less active and can sometimes even act as a refractory in oxidation atmospheres. Iron in high-fire reduction can yield lovely, delicate iron-blue and celadon green. High-fire, high-iron content glazes fired in reduction will yield glossy dark brown or brownish black. In thin areas, the iron may reoxidize during cooling. Reoxidization will result in those areas turning red or gaining red highlights. • 08of 11

Manganese Dioxide Manganese is usually introduced into glazes as manganese carbonate. Black manganese dioxide is more often used in slips and clay bodies, where its coarseness yields spots and splotches. Manganese, when compared to cobalt or copper, is a fairly weak colorant. It is toxic; handle with caution, using all safety precautions. o o

In high-alkaline glazes, manganese yields rich blue-purple or plum. At cone 6 and above, manganese produces brown.

3

o

In lead glazes, manganses yields soft purple tinged with brown. Extremely toxic; not for functional ware.

Nickel Oxide Nickel oxide, when used by itself, gives notoriously unpredictable results. It can be used to produce quiet grays and browns, but nickel is almost always used to modify and tone-down the colors produced by other colorants.

Rutile Rutile is an impure titanium ore containing some iron and other materials. It is a very interesting colorant which is generally tan in oxidation and gray in reduction. Rutile encourages crystal growth in mid-range and high-fire glazes. It is well known for creating lovely streaky and mottled effects. o o o

In boron-containing glazes rutile produces pronounced streaks or spots, especially in glazes containing other colorants. In fluid glazes, rutile encourages opalescent blues. Rutile increases opacity.

Other Colorants Other colorants that are used less often include: o o o o o

o o o

Antimony: used for yellow in low-fire glazes. Cium and Selenium: very similar, producing bright reds. Both burn out extremely easily. Toxic; not for functional ware. Gold: gives a range of pink, red and purple. Ilmenite: as a colorant, very similar to black iron oxide. Iron Chromate: produces shades of gray, brown and black. Iron chromate plus tin may produce a pink or reddish brown; if applied with a brush, can yield black hazed or haloed by pink. Toxic; handle with care. Platinum: gives gray. Silver and Bismuth: used in luster overglazes. Uranium Oxide: gives red, coral and yellow colors. Note: even fired into a glaze, uranium remains radioactive. Toxic; handle with care.

4

Ceramic Glaze Ingredients Transform Pottery Pieces Into Useable Art By Beth Peterson Updated 11/14/19

Yagi Studio / Getty Images Ceramic glazes protect and seal fresh pottery, making it both functional and beautiful. This vitreous compound can transform a porous bowl, cup, or plate into a food-safe and stain-resistant eating vessel. And glazing is fun, too— arguably the most exciting procedure in ceramic-making. Once a glaze is applied and the piece is fired—causing a chemical reaction and, often, a transformation in color—the outcome is magical. But creating fired pottery pieces is not all hocus-pocus. A basic understanding of glaze application and firing yields consistent and desirable results, as the key components of different glazes each have their own function.

Silica: The Glass-Former Silica (or industrial sand) is the key ingredient in glass, raw clay, and ceramic glazes. Silica can be obtained naturally from quartz, sandstone, sand, or flint, or it can be manufactured as silica oxide. When making your own glazes, products like quartz, flint, and pure silica can be added as the glass-former. In fact, if you get it hot enough, silica forms glass all by itself. However, silica's melting point (approximately 3100 F or 1710 C) is hotter than can be obtained by any ceramic kiln. Therefore, silica cannot be used on its own as a pottery sealer.

Alumina: The Refractory Nearly all glazes contain alumina, or aluminum oxide, which acts as a stiffening agent. Without alumina, the glaze would simply slide off the surface of any vertical piece as it's applied, which is not an ideal scenario. By adding alumina as a clay (kaolin, ball clay, or fireclay) or as alumina hydrate (a white manufactured powder), the glaze can stick to the pottery's surface without coming off. 5

Not only does alumina stiffen a glaze, but it also helps to disperse fine gas bubbles that can form in the firing process. Additionally, alumina enhances pink hues used in coloring the final piece.

Flux: The Melting Agent Fluxes play the key role in lowering the melting point of silica, making it usable in ceramic glazes. And, like silica, fluxes also promote vitrification (the transformation into glass). The most commonly used fluxes in ceramic glazes are obtained from limestone as calcium oxides. Potash feldspar and soda feldspar are good examples. Each flux works in its own peculiar way. Some are very active, allowing the glaze to mature at earthenware temperatures. Others are less active, and useful only when firing at mid- to high-range temperatures. It is important to note, however, that many of the metallic oxides used as fluxes are toxic and can be respired in their immature state. Use care and wear a dust mask when handling them. Also, make sure the final bowl, plate, or cup has reached full maturity to prevent any leaching into food served on or in it.

Colorant: The Beautifier Once melted, silica is transparent, making colorants necessary in order to achieve the wide range of hues that make decorating pottery with glazes so rewarding. Ceramic colorants must be able to withstand high temperatures without burning off so most are made from metallic oxides—a medium that can also affect the melting point of the glaze. Before firing, take into what colorant you are using and do the math to make sure your firing temperature is correct. Also, raw metal oxides usually bear no resemblance to the color they produce in the glaze. Knowing what minerals create which colors is key to making your end product yield the hue you are going for. In addition to colorants, other modifiers may be added to glazes that affect opacity, iridescence, or the working quality of the glaze when it's still raw (unfired).

6